Nonequilibrium microstructures and their evolution in a Fe-Cr-W-Ni-C laser clad coating

The laser-solidified microstructural and compositional characterization and phase evolution during tempering at 963 K were investigated using an analytical transmission electron microscope with energy dispersive X-ray analysis. The cladded alloy, a powder mixture of Fe, Cr, W, Ni, and C with a weight ratio of 10:5:1:1:1, was processed with a 3 kW continuous wave CO2 laser. The processing parameters were 16 mm/s beam scanning speed, 3 mm beam diameter. 2 kW laser power, and 0.3 g/s feed rate. The coating was metallurgically bonded to the substrate, with a maximum thickness of 730 mu m, a microhardness of about 860 Hv and a volumetric dilution ratio of about 6%. Microanalyses revealed that the cladded coating possessed the hypoeutectic microstructure comprising the primary dendritic gamma-austenite and interdendritic eutectic consisted of gamma-austenite and M7C3 carbide. The gamma-austenite was a non-equilibrium phase with extended solid solution of alloying elements and a great deal of defect structures, i.e. a high density of dislocations, twins, and stacking faults existed in gamma phase. During high temperature aging, in situ carbide transformation occurred of M7C3 to M23C6 and M6C. The precipitation of M23C6, MC and M2C carbides from austenite was also observed.

铁基抗高温磨损激光熔覆涂层强韧设计和研究II:Fe-Cr-C-W-Ni激光熔覆层的微观组织及性能

本文以对热工模具进行失效分析的基础上，利用激光熔覆技术，在５ＣｒＭｎＭｏ基础上设计并制备强韧兼备的抗高温磨损涂层。

裂纹顶端位错的运动和小范围屈服的K_(Ⅱc)

本文从裂纹顶端位错运动的简化模型估计形成塑性区所消耗的功;从而计算临界裂纹扩展力。由于Ⅰ型加载和Ⅱ型加载的应力状态有所不同,裂纹顶端塑性功耗也会不一样。基于上述思想,考虑了小范围屈服的K_(Ⅰc)和K_(Ⅱc)的关系,得出K(Ⅱc)>K(Ⅰc)的结论,符合实验结果;并就K(Ⅱc)/K(Ⅰc)的比值与材料性能和温度的关系作了讨论。

铁基抗高温磨损激光熔覆涂层强韧设计和研究 Ⅱ:Fe-Cr-C-W-Ni激光熔覆层的微观组织及性能

利用ＯＭ、ＳＥＭ、ＴＥＭ研究了Ｆｅ－Ｃｒ－Ｃ－Ｗ－Ｎｉ激光熔覆涂层熔覆态及其高温时效态的微观组织结构。结果表明激光熔覆层组织细小，具有强韧两相组成（奥氏体和Ｍ_７Ｃ_３碳化物）的微观结构特征，高温时效处理组织中有Ｍ_（２３）Ｃ_６、Ｍ_６Ｃ、Ｍ_２Ｃ等新碳化物形成。显微硬度和冲击磨损实验证实了激光熔覆态和峰值时效态熔覆层均具有良好的力学性能。